FeCrAl Ferro-Chromium-Aluminum D A1 Tk1 Apm High-Temperature Heating Resistance Wire

Detalles del producto

Place of Origin: Shanghai China

Nombre de la marca: TANKII

Certificación: ISO， ROHS

Model Number: APM

Pago y términos de envío

Minimum Order Quantity: 10 KG

Precio: Negociable

Packaging Details: wooden Case

Delivery Time: 25 days

Payment Terms: L/C,D/A,D/P,T/T,Western Union,MoneyGram

Supply Ability: 100 Tons/Month

Consiga el mejor precio

Contacta ahora

Especificaciones

Descripción

Especificaciones

Resaltar:

Material:	TK APM	Resistivity:	1.45
Diameter:	0.05-10.0mm	Surface:	Bright, Golden， Blue， oxidation etc.
sample:	accepted small order	HS Code:	72230000
Shape:	ribbon, round wire, flat wire, flat strip, rod, bar, pipe, tube,

Material:	TK APM
Resistivity:	1.45
Diameter:	0.05-10.0mm
Surface:	Bright, Golden， Blue， oxidation etc.
sample:	accepted small order
HS Code:	72230000
Shape:	ribbon, round wire, flat wire, flat strip, rod, bar, pipe, tube,

Descripción

FeCrAl Ferro-Chromium-Aluminum D A1 Tk1 Apm High-Temperature Heating Resistance Wire

This product takes refined master alloy as raw material, uses powder metallurgy technology to manufacture alloy ingots, and is manufactured by special cold and hot processing and heat treatment process. The product has the advantages of strong oxidation resistance, good corrosion resistance at high temperature, small creep of electro-thermal components, long service life at high temperature and small change of resistance. It is suitable for high temperature 1420 C, high power density, corrosive atmosphere, carbon atmosphere and other working environments. It can be used in ceramic kilns, high temperature heat treatment furnaces, laboratory furnaces, electronic industrial furnaces and diffusion furnaces.

(Wt%) Main Composition

	C	Si	Mn	Cr	Al	Fe
Min	-	-	-	20	5.5	Bal.
Max	0.04	0.5	0.4	22	6.0	Bal.

Main Mechanical Properties

Tensile Strength at Room Temperature	650-750MPa
Elongation Rate	15-25%
Hardness	HV220-260
Tensile Strength at 1000℃	22-27MPa
High Temperature Durability at 1000℃ and 6MPa	≥100h

Main Physical Properties

Density	7.1g/cm³
Resistivity	1.45×10^-6 Ω.m
Melting Point	1500℃
Maximum Continuous Working Temperature	1400℃
Resistance Temperature Coefficient(Ct)	800℃	1000℃	1400℃
Resistance Temperature Coefficient(Ct)	1.03	1.04	1.05
Average Linear Expansion Coefficient	20-800℃	20-1000℃	20-1400℃
Average Linear Expansion Coefficient	14	15	16

Fast life

1300℃

1350℃

Average Fast Life (Hours)

110

Sagging Rate After Rupture

Testing according to GB/T13300-91 standard method

FeCrAl Ferro-Chromium-Aluminum D A1 Tk1 Apm High-Temperature Heating Resistance Wire 0

Specifications

Wire diameter range φ0.1-10mm

Tags:

Buenos tubo/tubo del alambre 400 de la aleación de níquel de cobre de Monel de la resistencia a la corrosión para la torre de enfriamiento

Consiga el mejor precio

Alambre de manganina Tankii Nuevo Inventario / Aleación 290 / manganina 43 0.134mm Superficie Brillante Para Resistor de Alta Precisión

Consiga el mejor precio

El video

Por favor envíenos su petición y le contestaremos cuanto antes.

Envíe

Cobre alambre de aleación de níquel

Alambre de resistencia eléctrica

Alambre desnudo del termopar

Aleación de Fecral

Cable de termopar

Aleación de Nicr

Alambre termal del espray

Elemento de calefacción del horno

Aleación de la precisión

Leguras de cobre

Las demás:

Alambre esmaltado

Aleación da alta temperatura

Conector de termopar

FeCrAl Ferro-Chromium-Aluminum D A1 Tk1 Apm High-Temperature Heating Resistance Wire

aleación del cobre y del níquel,

aleación de cobre del níquel,

aleación del cobre y de níquel

Buenos tubo/tubo del alambre 400 de la aleación de níquel de cobre de Monel de la resistencia a la corrosión para la torre de enfriamiento

Estabilidad del alambre resistente eléctrico de cobre del manganeso buena para el resistor del emisor

Fecral resistohm145 A1 D A1 Tk1 APM High-Temperature Heating Wire